中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 31 No. 6 June 2021 |
（1. Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China;
2. Science and Technology on Reactor System Design Technology Laboratory, Nuclear Power Institute of China, Chengdu 610213, China）
Abstract:Two kinds of semi-solid samples of AZ80-0.2Y-0.15Ca (wt.%) (AZ80M) magnesium alloy were prepared by semi-solid isothermal heat treatment of materials with and without equal channel angular pressing (ECAP) process. The microstructures of initial and semi-solid treated samples were compared and analyzed. The results showed a significant difference in the liquid phase distribution between three-pass ECAP processed (3P) and as-received samples during the isothermal heating process. The semi-solid 3P sample showed a more uniform liquid distribution due to its smaller dihedral angle. Besides, the coarsening processes of solid grains of as-received and 3P samples were dominated by the coalescence and Ostwald ripening mechanism, respectively. The difference of coarsening processes was mainly related to the proportion of the high-angle grain boundaries in materials, which further affected the evolution behavior of the liquid pools.
Key words: AZ80M; equal channel angular pressing; semi-solid microstructure; liquid phase distribution; coarsening mechanism