中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 29 No. 3 March 2019 |
（1. Key Lab of Biometallurgy of Ministry of Education of China, School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, China;
2. CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640, China;
3. College of Science, Hunan University of Technology, Zhuzhou 412000, China;
4. Beijing Synchrotron Radiation Facility, Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049, China）
Abstract:Bioleaching of chalcopyrite with different crystal structures (α-phase, β-phase and γ-phase) by Acidianus manzaensis was comparatively studied by synchrotron radiation based X-ray diffraction (SR-XRD) and S K-edge X-ray absorption near edge structure (XANES) spectroscopy. The α-phase, β-phase and γ-phase chalcopyrite was prepared by heating original chalcopyrite at 583, 773 and 848 K, respectively. Bioleaching results showed that [Cu2+] in the leaching solution of α-phase, β-phase, γ-phase and original chalcopyrite after 10 days of bioleaching was 1.27, 1.86, 1.43 and 1.13 g/L, respectively, suggesting that β-phase had a better leaching kinetics than others. SR-XRD and XANES results indicated that jarosite and chalcopyrite were the main components in the leaching residues in all cases, and elemental sulfur formed in the early stage of bioleaching. While for β-phase and γ-phase chalcopyrite during bioleaching, bornite was produced in the initial stage of leaching, and turned into chalcocite on day 6.
Key words: chalcopyrite; crystal structure; bioleaching; Acidianus manzaensis; SR-XRD; XANES