(1. 國家冷軋板帶裝備及工藝工程技術(shù)研究中心，秦皇島 066004; 2. 燕山大學(xué) 機械工程學(xué)院，秦皇島 066004)
摘 要: 采取只加熱鈦層的方法實現(xiàn)協(xié)調(diào)變形軋制制備鈦/鋁復(fù)合板，通過剪切實驗、金相顯微鏡、掃描電子顯微鏡，研究壓下率、鈦層加熱溫度對鈦/鋁復(fù)合板的厚比分配、剪切強度和界面的影響。結(jié)果表明：隨著鈦層溫度的升高和總軋制壓下率的增大，鈦鋁復(fù)合板的鈦層和鋁層變形率差值逐漸減小；當(dāng)溫度為800 ℃，軋制壓下率為50%時，鋁層和鈦層的變形率分別達到了51.4%和 48.6%，鈦鋁復(fù)合板變形趨于協(xié)調(diào)。鈦與鋁的結(jié)合界面剪切強度達到107.5 MPa，基本接近鋁基體的剪切強度。加熱過程中鈦板表面會產(chǎn)生氧化層，但是在較大軋制壓下率下，鈦的氧化層會撕裂，金屬鋁擠入裂縫與新鮮鈦金屬接觸，在強大壓力和高溫作用下，鈦、鋁元素相互擴散從而達到牢固的冶金結(jié)合。
關(guān)鍵字: 鈦/鋁復(fù)合板；軋制；協(xié)調(diào)變形；剪切強度；氧化層
（1. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Qinhuangdao 066004, China; 2. College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, China）
Abstract:The Ti/Al composite plate was prepared by the method of only heating titanium layer. The effects of the rolling reduction and Ti layer heating temperature on the shear strength, interface and distribution of thickness ratios of Ti/Al clad plates were investigated by shear experiments, metallographic microscopy and scanning electron microscopy. The results show that with the increase of the temperature of the titanium layer and the total rolling reduction, the difference between the titanium layer and the aluminum layer deformation of the Ti/Al composite plate decreases gradually. When the temperature is 800 ℃ and the reduction is 50%, the reduction of aluminum layer and titanium layer reaches 51.4% and 48.6%, respectively. And the deformation of titanium/aluminum composite plate tends to become coordinated. The interfacial shear strength of titanium and aluminum reaches 107.5 MPa, which is close to the shear strength of aluminum matrix. During the heating process, an oxide layer is produced on the surface of the titanium plates. However, the oxide layer is completely broken with a large rolling reduction, and then, aluminum metal extruded into the cracks and made contact with fresh titanium metal. Under the action of high pressure and high temperature, Ti and Al atoms mutually diffuse so that the Ti/Al clad plates achieved a strong metallurgical bond.
Key words: Ti/Al clad plate; rolling; coordination deformation; shear strength; oxide layer