中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 28 No. 1 January 2018 |
（1. School of Materials Science and Engineering, Shandong University, Ji’nan 250061, China; 2. School of Materials Science and Engineering, Shandong University of Technology, Zibo 255000, China）
Abstract:For enhancement of mechanical properties in Mg-9Li-3Al alloys, Mg-9Li-3Al duplex alloys were alloyed by addition of Sn and Y. Microstructure evolution and mechanical property response of as-cast Mg-9Li-3Al alloys by alloying with Sn and Y were investigated by optical microscopy, scanning electron microscopy, X-ray diffractometry and tensile tests. The results indicate that considerable blocky dendrites of primary α phase in Mg-9Li-3Al alloys become lath-like due to the addition of Sn. With addition of Y, Mg-9Li-3Al alloy consists of both block-like and lath-like α-Mg dendrites. The as-cast Mg-9Li-3Al-1Sn-1Y alloy shows a yield strength of 118 MPa, ultimate tensile strength of 148 MPa and the elongation to failure of 21%. Improvement in both strength and elongation of Mg-9Li-3Al alloys with Sn and Y addition is attributed to the combined action of MgLi2Sn and Al2Y intermetallic compounds.
Key words: Mg-Li alloys; grain structure; tensile properties; precipitation strengthening