中國有色金屬學(xué)報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 26 No. 4 April 2016 |
（1. School of Materials Science and Engineering,
Henan University of Science and Technology, Luoyang 471023, China;
2. State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,
Chinese Academy of Sciences, Lanzhou 730000, China;
3. Collaborative Innovation Center of Nonferrous Metals of Henan Province, Luoyang 471023, China）
Abstract:The electrochemical and corrosion-wear behaviors of TC4 alloy in artificial seawater were studied. And the influences of electrochemical state on passive behavior, failure mechanism of passive film and corrosion-wear synergy were emphatically analyzed. The corrosion-wear analysis of the alloy was fulfilled by methods of mass loss, electrochemical testing and scanning electron microscope (SEM). It can be observed that the cathodic shift of open circuit potential and three order of magnitude increase of current density can be obtained during corrosion-wear process. Total corrosion-wear loss increases with increasing applied potential, confirming the synergy between wear and corrosion. High polarisation potential results in low coefficient of friction and high corrosion rate. The relative contribution of pure mechanical wear to total material loss deceases obviously with the increase of potential from open circuit potential to 0.9 V during corrosion-wear. Contributions of wear-induced-corrosion and corrosion-induced-wear are significant especially at higher potentials.
Key words: TC4 alloy; corrosion-wear; electrochemical state; synergistic effect