Abstract:Thick-film thermistor with negative temperature coefficient (NTC), low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of with Ba_0.5Bi_0.5Fe_0.9Sn_0.1O₃. The electrical properties of the thick films were characterized by a digital multimeter, a Keithley 2400 and an impedance analyzer. The results show that with the Ba_0.5Bi_0.5Fe_0.9Sn_0.1O₃ content increasing from 0.05 to 0.25, the values of room-temperature resistivity, thermistor constant and peak voltage of the thick films increases and are in the ranges of 1.47-26.5 Ω·cm, 678-1345 K and18.9-47.0 V, respectively. The corresponding currentat the peak voltage of the thick films decreases and is in the range of 40-240 mA. The impedance spectroscopy measurement demonstrates that the as-prepared thick films show the abnormal electrical heterogeneous microstructure, consisting of high-resistive grains and less resistive grain boundary regions. It can be concluded that the addition of Ba_0.5Bi_0.5Fe_0.9Sn_0.1O₃ into improves the thermistor behavior and but also deteriorates the current characteristics.

Key words: NTC thick films; ; Ba_0.5Bi_0.5Fe_0.9Sn_0.1O₃; electrical property