中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 24 No. 10 October 2014 |
（1. Analytical and Testing Center, Sichuan University, Chengdu 610064, China;
2. School of Manufacturing Science and Engineering, Sichuan University, Chengdu 610065, China）
Abstract:The effect of recovery heating rate on shape memory effect of the up-quenched Cu-8.88Al-10.27Mn (mass fraction, %) alloy was investigated by optical microscopy, electron transmission microscopy (TEM) and electrical resistivity measurement. It is found that the shape recovery rate decreases as the heating rate decreases. It can reach 75% when the heating rate is 20 °C/min, while it is only 8% when the heating rate is 1 °C/min. In situ microstructure observation indicates that the dependence of shape memory effect on recovery heating rate is caused by the stabilization of twinned martensite induced by deformation. The analysis of electrical resistivity shows that the stabilization of twinned martensite may be ascribed to formation of compound defects of vacancies and dislocations at the boundaries of twinned martensite during the slow heating. The compound defects prevent the reverse transformation of twinned martensite.
Key words: Cu-Al-Mn alloy; shape memory effect; martensitic phase transformation; twinning