摘 要: 利用示差掃描量熱儀(DSC)分析方法，研究了快凝 Al-Fe-(Cr，Mo)-Si合金中準晶相的轉(zhuǎn)變動力學特征。結(jié)果表明：采用Jeziorny 數(shù)學模型對準晶相的轉(zhuǎn)變非等溫DSC曲線進行分析，其轉(zhuǎn)變動力學特征參數(shù)表征的物理意義與透射電鏡(TEM)的分析結(jié)果基本一致。因此，建立了宏觀分析與微觀顯微組織之間的內(nèi)在聯(lián)系。
關(guān)鍵字: 快速凝固 準晶相 DSC 轉(zhuǎn)變動力學
（1.School of Materials Science and Engineering,
Zhengzhou Univer sity of Technology, Zhengzhou 450002
2.School of Materials Science and Engineering,
University of Science and Technology Beijing, Beijing 100083）
Abstract:Differential Scanning Calorimetry (DSC) was used to study kinetic charateristics of transformation on quasicrystalline phases in a rapidly solidified Al-Fe-(Cr, Mo)-Si alloy. It is shown that the description of kinetic parameters on transformation of quasicrystalline phases is basically consistent with the results of TEM analysis, by analysing the non-isothermal DSC curves of quasicrystalline phases transformation by Jeziorny's mathematical model. Therefore, the internal relations between kinetic parameters and microstructures of materials have been built up.
Key words: rapid solidification quasicrystalline phase DSC kinetics of transformation