(中南工業(yè)大學(xué)非平衡材料研究所， 長沙 410083)
摘 要: 制備了含微量磷元素的Al-22Si合金粉末。研究了粉末形貌、粒度大小與分布，以及粉末顯微組織，并初步探討了微量磷對合金粉末特性影響的機理。結(jié)果表明，微量磷元素降低了粉末氧含量。其中含0.04%磷的快冷Al-22Si合金粉末球形粉末較高，平均粒度最小，粉末中初晶硅得到了進一步細化。
關(guān)鍵字: 快速凝固 鋁-硅合金 磷 顯微組織
（Non-equilibrium Materials Research Institute, Central South University of Technology, Changsha 410083）
Abstract:Several Al-22Si alloy powders with additions of trace phosphorus were prepared by rapid solidification, and powder morphology, size and distribution, microstructure and the effect mechanism of trace phosphorus on alloy powder characteristics have been investigated. It was concluded that the additive phosphorus decrease the oxygen content of the powder, and the RS Al-22Si alloy containing 0.04% phosphorus provides more ball-like powders, smaller average size, more refined primary silicon phases.
Key words: rapid solidification aluminium-silicon alloy phosphorus microstructure