Zn-27Al-1Cu alloy by spray forming process
(Beijing General Research Institute for Nonferrous Metals,
Beijing 100088, P.R.China)
Abstract:Producing process of spray formed Zn-27Al-1Cu billets, hot extrusion process and producing process of sliding bearing were studied. The microstructure, properties and wearability of spray formed Zn-27Al-1Cu billets were also studied. The results of experiments and application show that the strength of hot extruded Zn-27Al-1Cu from spray forming process is much better than those of Babbit and cast ZA27 alloy. The durability of new type sliding bearing is 150% more than that of conventional one.
Key words: spray forming; Zn-27Al-1Cu alloy; cast ZA27 alloy; sliding bearing