中國有色金屬學(xué)報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 22 No. 6 June 2012 |
（1. College of Biological and Chemical Engineering, Jiaxing University, Jiaxing 314001, China;
2. State Key Laboratory Breeding Base of Green Chemistry-Synthesis Technology,
College of Chemical Engineering and Materials Science, Zhejiang University of Technology, Hangzhou 310032, China;
3. Key Laboratory of Clean Chemical Process of Jiaxing, Jiaxing 314001, China）
Abstract:The electrochemical behavior of lithium incorporated in aluminum electrode in LiTFSI/KTf (lithium bis (trifluoromethylsulfonyl) amide/CF3SO3K) molten salt electrolyte was studied by a variety of electrochemical techniques including cyclic voltammetry, chronopotentiometry and chronoamperometry. The reduction reaction is found involving a nucleation process on the aluminum electrode. The results of chronopotentiometry indicate that the process of lithium incorporation in aluminum is smooth and uniform. The galvanostatic cycle experiments show that the coulombic efficiency is very low in the first cycle, which is mainly due to the “retention capacity” of Li-Al alloys. This characteristic is testified by the results of XRD and SEM. The results of chronoamperometry indicate that the incorporation of lithium into aluminum for the formation of a-phase Li-Al alloy is limited by its diffusion rate, with a measured diffusion coefficient of 1.8×10-10 cm2/s.
Key words: molten salt; aluminum electrode; cyclic voltammetry; coulombic efficiency; nucleation process