2219-T87 Al alloy welding
（1. Thanthai Periyar Government Institute of Technology, Vellore-632002, India;
2. Government College of Engineering, Perumalpuram, Tirunelveli-627007, India）
Abstract:Fracture data of both parent metal and weldment metals from surface cracked tensile plates made of 2219-T87 Al alloy at cryogenic temperatures were correlated using a modified inherent flaw model. Fracture parameters to generate the failure assessment diagram were determined for the material. Fracture analysis was carried out considering the ultimate tensile strength value and the fracture data of aluminium base metal and weldment metal generated from center–surface cracked tensile specimens having different thicknesses. The failure assessment diagram of a material generated from tensile fracture plate configuration can be applied to failure pressure estimation of any cracked component, made of the same material.
Key words: centre through crack; tensile specimen; failure assessment diagram; fracture strength; inherent flaw model; 2219-T87 Al alloy