Abstract:Two micron SiC particles with angular and spherical shape and the sub-micron Al₂O₃ particles with spherical shape were introduced to reinforce 6061 aluminium by squeeze casting technology. Microstructures and effect of thermal-cooling cycle treatment (TCCT) on the thermal expansion behaviors of three composites were investigated. The results show that the composites are free of porosity and SiC/Al₂O₃ particles are distributed uniformly. Inflections at about 300 °C are observed in coefficient of thermal expansion (CTE) versus temperature curves of two SiC_p/Al composites, and this characteristic is not affected by TCCT. The TCCT has significant effect on thermal expansion behavior of SiC_p/Al composites and CTE of them after 3 cycles is lower than that of 1 or 5 cycles. However, no inflection is observed in Al₂O_3p/Al composite, while TCCT has effect on CTE of Al₂O_3p/Al composite. These results should be due to different relaxation behavior of internal stress in three composites.

Key words: SiC; aluminum matrix composite; thermal expansion behavior; thermal-cooling cycle treatment