中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 20 Special 2 July 2010 |
ZHANG Zhi(張 志)1, LI Lei(李 雷)1, WANG Li-min(王立民)3
（1. School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, China;
2. Key Laboratory of Automobile Materials, Ministry of Education, Jilin University, Changchun 130025, China;
3. State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry,
Chinese Academy of Sciences, Changchun 130022, China）
Abstract:Mg-10Ho-0.6Zr-xNd (x=0, 1, 3 and 5, mass fraction, %) alloys were prepared by metal mould casting, and the microstructures and mechanical properties were investigated. The results show that the grain size of as-cast alloys reduces and the hardness and strength increase with the increase of Nd content. The alloys are aged followed by solid solution treatment. Mg-10Ho-0.6Zr-3Nd and Mg-10Ho-0.6Zr-5Nd alloys exhibit obvious age hardening response. The hardness value of Mg-10Ho-0.6Zr-5Nd alloy increases from HV104 at as-cast state to HV136 at peak-aged state. The maximum ultimate tensile strength and yield strength of the Mg-10Ho-0.6Zr-5Nd alloy are obtained in at peak-aged state, and the values are 323 MPa, 212 MPa at room temperature, and 258 MPa, 176 MPa at 250 ℃, respectively. The improvement of the tensile strength is mainly attributed to the fine and dispersively distributed plate-shaped β′ metastable phase.
Key words: Mg-Ho-Zr-Nd alloy; microstructure; age hardening behavior; mechanical properties