中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 35 No. 10 October 2025 |
（1. School of Materials Science and Engineering, Shandong University of Technology, Zibo 255000, China;
2. Shandong Nanshan Aluminum Co., Ltd., Longkou 265700, China;
3. College of Machine, Shanghai Dianji University, Shanghai 201306, China;
4. Linqu Inspection and Testing Center, Linqu 262600, China）
Abstract:The microstructure and texture evolutions during extrusion and rolling processes of the 2195 Al-Li alloy were investigated. The EBSD technique was employed to reveal the microscopic evolution mechanisms of different texture components. The findings reveal that the texture evolution is governed by two mechanisms: an overall orientation transformation induced by plastic strain and a localized transformation occurring at the shearing bands within grains. During the rolling process, the extrusion texture components of Ex and Cu evolve into S , and the Bs rotates into the orientations near R-Bs and S. With increasing deformation, the S, Bs, and R-Bs orientations further rotate around the TD axis and disperse into new orientations, forming recrystallized grains. The shearing bands with different initial orientations exhibit similar orientation evolution patterns, all of which evolve from the initial orientation to a series of recrystallization orientations.
Key words: Al-Li alloy; texture evolution; grain orientation; extrusion and rolling processes; microstructure