中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 33 No. 8 August 2023 |
（1. Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;
2. School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, China;
3. Capital Aerospace Machinery Corporation Limited, Beijing 100076, China;
4. Department of Manufacturing Engineering, Technical University of Cluj-Napoca, Cluj-Napoca 400641, Romania）
Abstract:A filling roll bending process of a 2A12 aluminum alloy integral panel with polypropylene as filler was studied. The operating effect of filler was revealed, based on analytical, numerical, and experimental methods. The results show that the position difference of the neutral layer between the ribs and the web of the integral panel leads to the error of generatrix straightness, and the filler can reduce this difference. A certain range of the width gap (1-3 mm) between filler and rib can avoid the instability of the rib and the curl of the filler. The height gap between filler and rib determines the compression degree of filler. The best pressure transmission effect can be achieved as the filler is still higher than the rib (1 mm) after compression. The elastic modulus of filler slightly affects the forming accuracy of the integral panel within a certain range (450-1300 MPa). Still, the filler transfers insufficient pressure under lower elastic modulus (50 MPa) and limits the deformation of the integral panel under higher elastic modulus (20 GPa). Experimentally measured generatrix straightness verified the operating effect of filler.
Key words: integral panel; roll bending; filler; neutral layer; generatrix straightness